Photoluminescent
epoxy floor paint
Photoluminescent
epoxy floor paint is solvent-free, environmentally-friendly
product made up of two parts, 100% solidified.
Part A is luminous material, part B is solidified material.
Before using, part A should be stirred evenly, then exactly
weight Part A and Part B and mix them together according
to certain ratio. The best way to use the mixture is to
shave, or you can brush. It is suggested that white paint
with good adhesion be used as premier paint in order to
improve luminous effect. The residual of Part A and Part
B should be sealed separately and be kept from inter-contamination.The
appliances of the two parts should be separately used and
deposited. The activated time of the mixture of the two
parts is more than 2 hours. To avoid loss caused by solidifying,
it should be used up as soon as possible. The surface dry
is more than 4 hours, while whole dry takes over 24 hours.
The suggested quantity is 800-1000g/Sq.m when the paint
layer thickness is around 80 micron.
Performance
Index
Index
Item |
Luminance after
1 min
 ≥
|
Luminance after
60 min
≥
|
After glow time
(min) ≥
|
|
HG-D25
|
1400
|
30
|
3500
|
|
HB-D25
|
1000
|
35
|
5000
|
Technical
Index
|
Item
|
unit
|
Index
|
|
Flowing
evenly ≤
|
S
|
30
|
|
Rigidity
≥
|
S
|
0.55
|
|
Impulse
Intensity
|
|
No
crack, no peel , no obvious change
|
|
Abrasion
Resistance ≤
|
mg
|
11
|
|
Bibulous
rate ≤
|
%
|
0.30
|
|
Adhesion
≥
|
degree
|
2
|
|
Hydrochloric
Acid-resistance 20% ≥
|
|
30
days, no obvious change
|
|
Sulphuric
Acid-resistance 30% ≥
|
|
30
days, no obvious change
|
|
Phosphonic
Acid-resistance 5% ≥
|
|
30
days, no obvious change
|
|
Soda
Hydroxide-resistance 20% ≥
|
|
30
days, no obvious change
|
|
Oil-resistance
|
|
30
days, no obvious change
|
|
Acetate-resistance
25% ≥
|
|
20
hours, no obvious change
|
|
Nitric
Acid-resistance
|
|
Note:In normal
temperature enviroment,it can be stored for 6 months in
a storehouse and be kept from water,fire and direct sunlight.
|